PARAMESWARAN P, Saravanan Sekar, Malathy Paulpandi, Rameshbabu Rameshbabu, Susheela N and Navaneethakrishnan G
Mots-clés : Mg-6Zn-4Cu-2Ca-1Mn, Characterization, Mechanical Properties, uniform corrosion, SEM & EDS morphology, Electronegativity
Résumé :
<p>Stir-casting was done for manufacturing of
Mg-6Zn alloy by adding Ca, Cu and Mn in micron sizes (44 microns). The phases formed and the surface morphology was
analyzed with scanning electron microscope (SEM) equipped with energy
dispersive spectroscopy (EDS), X-ray diffraction (XRD) followed by mechanical tests. The different phases found in the alloy enhances
the strength of the material. When compared with other heat treated, RE
included and mechanically worked alloys, Mg-6Zn exhibits better result. During
the solidification process grain boundaries are formed due to higher denser
intermetallic, thus the corrosion result proves as a better option for the alloys
to be used in vehicles structural elements. <br></p>
Comme vous n'êtes pas connecté(e) au journal, notre politique est désormais d'afficher une version « texte seul » du/de la preprint. Cette version est obtenue en extrayant le texte du fichier PDF ou HTML, et rien ne garantit qu'elle soit une image fidèle du texte de l'article. La version texte seul est destinée à servir de référence pour les moteurs de recherche lorsqu'ils indexent le site, et elle n'est pas conçue pour être lue par des humains !