Mots-clés : Corrosion, Powder Metallurgy, Amorphous Alloy Powder, Passive Film
Résumé :
<p>In
this study, the corrosion behavior of a Fe-Cr-Mo-B-C alloy which was fabricated
by spark plasma sintering of an amorphous alloy powder, in 3.5% NaCl solution was
analyzed. Electrochemical impedance spectroscopy and potentiodynamic
polarization are techniques which were used for electrochemical performance
estimation of samples and the results were further compared with conventional
alloys: 1080 carbon steel and 304 stainless steel. Corrosion surface products
were characterized through scanning electron microscopy,
energy dispersive x-ray spectroscopy and x-ray photoelectron spectroscopy.
Specimens sintered at 800⁰C (S1-800) had achieved 94% densification
approximately while the sample sintered at 900⁰C (S2-900), had densified more which was 98%
approximately. S2-900 had better corrosion resistance than S1-800 while in
comparison to conventional alloys; it was inferior to 304 stainless steel. It was concluded that the increase in density of
sintered samples favoured the formation of more uniform surface products and
enhanced the formation of the passive chromium oxide (Cr<sub>2</sub>O<sub>3</sub>)
layer.<br></p>
Comme vous n'êtes pas connecté(e) au journal, notre politique est désormais d'afficher une version « texte seul » du/de la preprint. Cette version est obtenue en extrayant le texte du fichier PDF ou HTML, et rien ne garantit qu'elle soit une image fidèle du texte de l'article. La version texte seul est destinée à servir de référence pour les moteurs de recherche lorsqu'ils indexent le site, et elle n'est pas conçue pour être lue par des humains !