effects of chloride ion on corrosion rate of mild steel in sulphuric acid pickling
solutions was investigated using hydrogen evolution method. Sodium chloride
salt was used to furnish the chloride ion. The results show increasing
reduction in corrosion rate of mild steel in sulphuric acid pickling at all
concentrations with increasing amount of sodium chloride salt, thereby
confirming that the chloride ion has an inhibitive effect on the hydrogen
evolution reaction in acid pickling of mild steel and so could serve as an
inhibitor in a typical sulphuric acid pickling of mild steel.</i></p>
<p>
<i><br clear="all" style="page-break-before:always;mso-break-type:section-break"></i></p>
Da Sie nicht beim Journal angemeldet sind, ist es nun unsere Richtlinie, eine 'Nur-Text'-Version des/der preprint anzuzeigen. Diese Version wird durch Extraktion des Textes aus der PDF- oder HTML-Datei erstellt, und es ist nicht garantiert, dass der Text ein originalgetreues Abbild des Textes des Artikels ist. Die Nur-Text-Version soll als Referenz für Suchmaschinen bei der Indexierung der Website dienen und ist nicht dafür gedacht, von Menschen gelesen zu werden!
Wenn Sie die für Menschen lesbare Version des/der preprint ansehen möchten, registrieren Sie sich bitte (falls noch nicht geschehen) und melden Sie sich an. Die Registrierung ist völlig kostenlos.