effects of chloride ion on corrosion rate of mild steel in sulphuric acid pickling
solutions was investigated using hydrogen evolution method. Sodium chloride
salt was used to furnish the chloride ion. The results show increasing
reduction in corrosion rate of mild steel in sulphuric acid pickling at all
concentrations with increasing amount of sodium chloride salt, thereby
confirming that the chloride ion has an inhibitive effect on the hydrogen
evolution reaction in acid pickling of mild steel and so could serve as an
inhibitor in a typical sulphuric acid pickling of mild steel.</i></p>
<p>
<i><br clear="all" style="page-break-before:always;mso-break-type:section-break"></i></p>
Comme vous n'êtes pas connecté(e) au journal, notre politique est désormais d'afficher une version « texte seul » du/de la preprint. Cette version est obtenue en extrayant le texte du fichier PDF ou HTML, et rien ne garantit qu'elle soit une image fidèle du texte de l'article. La version texte seul est destinée à servir de référence pour les moteurs de recherche lorsqu'ils indexent le site, et elle n'est pas conçue pour être lue par des humains !
Si vous souhaitez consulter la version lisible du/de la preprint, veuillez vous inscrire (si ce n'est pas déjà fait) puis vous connecter. L'inscription est entièrement gratuite.