Schlüsselwörter: Stainless steel; chloride; pitting corrosion; electrochemistry; materials issues and radiation
Zusammenfassung:
<p class="MsoNormal">Chloride ions in the marine environment and
body fluid solutions are the leading cause of pitting corrosion in stainless
steel (SS). In this study, pitting corrosion of SS 304L was prevented by using grain
refinement and gamma-ray irradiation. A solution annealed SS 304L was 90%
severe plastic deformed at liquid N2 temperature, followed by annealing, and
gamma-ray irradiation was performed separately. Further, a series of
electrochemical corrosion tests were carried out in a simulated marine
environment and body fluid solution to check the resistibility against pitting
corrosion. Breakdown potential due to pitting was observed for all samples in
both solutions, except for the gamma-ray irradiated rolled specimen. Pit size
and morphology were characterized by using Confocal Laser Scanning Microscopy
(CLSM).</p>
Da Sie nicht beim Journal angemeldet sind, ist es nun unsere Richtlinie, eine 'Nur-Text'-Version des/der preprint anzuzeigen. Diese Version wird durch Extraktion des Textes aus der PDF- oder HTML-Datei erstellt, und es ist nicht garantiert, dass der Text ein originalgetreues Abbild des Textes des Artikels ist. Die Nur-Text-Version soll als Referenz für Suchmaschinen bei der Indexierung der Website dienen und ist nicht dafür gedacht, von Menschen gelesen zu werden!