Mots-clés : Stainless steel; chloride; pitting corrosion; electrochemistry; materials issues and radiation
Résumé :
<p class="MsoNormal">Chloride ions in the marine environment and
body fluid solutions are the leading cause of pitting corrosion in stainless
steel (SS). In this study, pitting corrosion of SS 304L was prevented by using grain
refinement and gamma-ray irradiation. A solution annealed SS 304L was 90%
severe plastic deformed at liquid N2 temperature, followed by annealing, and
gamma-ray irradiation was performed separately. Further, a series of
electrochemical corrosion tests were carried out in a simulated marine
environment and body fluid solution to check the resistibility against pitting
corrosion. Breakdown potential due to pitting was observed for all samples in
both solutions, except for the gamma-ray irradiated rolled specimen. Pit size
and morphology were characterized by using Confocal Laser Scanning Microscopy
(CLSM).</p>
Comme vous n'êtes pas connecté(e) au journal, notre politique est désormais d'afficher une version « texte seul » du/de la preprint. Cette version est obtenue en extrayant le texte du fichier PDF ou HTML, et rien ne garantit qu'elle soit une image fidèle du texte de l'article. La version texte seul est destinée à servir de référence pour les moteurs de recherche lorsqu'ils indexent le site, et elle n'est pas conçue pour être lue par des humains !